The mixtures were premixed in a highspeed mixer for 5min, plasticized on a tworoll mill at a constant temperature (160°C), then molded in a compression molding machine at 160°C for 5min and cooled for 3min under pressure of 10 MPa into sheets of (2±) mm thickness for structure characterization and property measurement.